MAGNUM™ 3513
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l7lm3D_MAGNUM-3513.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM* 3513 is a grade which combines high impact with good flowability. It is suitable for injection moulding and extrusion applications. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.05 | g/cm³ | ISO 1183/B |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | |||
| 220°C/10.0 kg | 8.60 | cm³/10min | ISO 1133 |
| 220°C/10.0 kg | 8.00 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 3 | ||
| Saturation | 0.70 | % | |
| Equilibrium | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm, Injection Molded | 2360 | MPa | ISO 527-2 |
| -- | 2600 | MPa | ISO 527-2 4 |
| Tensile Stress | |||
| Yield, 3.20 mm, Injection Molded | 46.0 | MPa | ISO 527-2/50 |
| Yield | 47.0 | MPa | ISO 527-2 5 |
| Tensile Strain | |||
| Yield, 3.20 mm, Injection Molded | 2.3 | % | ISO 527-2/50 |
| Yield | 2.4 | % | ISO 527-2 6 |
| Nominal strain at break | 40 | % | ISO 527-2 7 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2200 | MPa | ISO 178 |
| Flexural Stress (3.20 mm, Injection Molded) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 8.0 | kJ/m² | ISO 179/2C |
| -30°C, Injection Molded | 11 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 24 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 15 | kJ/m² | ISO 179/2C |
| -30°C | 11.0 | kJ/m² | ISO 179/1eA 8 |
| 23°C | 22.0 | kJ/m² | ISO 179/1eA 9 |
| Charpy impact strength | ISO 179/1eU 10 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 11 | kJ/m² | |
| 23°C, Injection Molded | 23 | kJ/m² | |
| Tensile notched impact strength (23°C) | 72.0 | kJ/m² | ISO 8256/1 11 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa | 103 | °C | ISO 75-2 12 |
| 1.8 MPa, Annealed | 100 | °C | ISO 75-2/A |
| 1.8 MPa | 100 | °C | ISO 75-2 13 |
| Vicat Softening Temperature | |||
| -- | 101 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 99.0 | °C | ISO 306 14 |
| CLTE | ISO 11359-2 15 | ||
| Flow | 8.0E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 16 |
| Relative Permittivity | IEC 60250 17 | ||
| 100 Hz | 2.80 | ||
| 1 MHz | 2.70 | ||
| Dissipation Factor | IEC 60250 18 | ||
| 100 Hz | 6.0E-3 | ||
| 1 MHz | 8.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 19(2.00 mm) | 45 | mm/min | ISO 3795 |
| Flame Rating 20 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | ISO 1210 21 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 20 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9653-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NILENE® E8 | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| FRAGOM PR/900 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| HiFill® PA6 GF30 RM BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Larton K/20 | LATI S.p.A. | PPS | Larton |