Order Products : sales@su-jiao.com
VITAMIDE® AT37BK6318
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l7ffi7_VITAMIDE-AT37BK6318.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® AT37BK6318 is a Polyamide 66 (Nylon 66) product filled with 33% glass fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 130 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 200 | MPa | ISO 178 |
| Break | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 16 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 16.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | 78.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 78 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 250 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 2.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 34 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 450 | V | IEC 60112 |
| -- 3 | 450 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2102N3W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Daelim Po1y® DHC-1 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| DINALON® A1X25 HI | Grupo Repol | Nylon 66 | DINALON® |
| Pearlbond™ 121 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| Sylvin 8773-60D Natural | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |