Edgetek™ ET9700-5012 NHFR Natural
| Category: | PPA , Polyphthalamide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l7YWTD_Edgetek-ET9700-5012-NHFR-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high reflectivity, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on selected engineering thermoplastic resins which are compounded with reinforcing additives such as glass fiber and mineral fillers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.10 to 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | > 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded, Complete Break) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | > 30 | kJ/m² | ISO 179 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (3.00 mm) | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 290 to 330 | °C | |
| Mold Temperature | 130 to 160 | °C | |
| Screw Speed | 50 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell RP374R | LyondellBasell Industries | PP Random Copolymer | Purell |
| Shinko-Lac® ABS VM-1 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Flontech® FT-BRR40-M5-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| SHINSTRA WG20TKB | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |
| Hostacom ERC 198N G81493 | LyondellBasell Industries | PP Copolymer | Hostacom |