Ultramid® B3WG6 GIT BK807
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l7XIqT_Ultramid-B3WG6-GIT-BK807.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3WG6 GIT BK807 is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade offering excellent flow characteristics, UV stability and is paintable. Applications Typical applications include door handles, roof racks and power tools. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 6.6 | % | |
| Equilibrium, 23°C, 50% RH | 2.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9400 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ANYPOL CL-2000F | SH Energy & Chemical | PS (EPS) | ANYPOL |
| EPO-TEK® OE188 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| HiFill® PA6 GF60 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina IVORY PVC COMPOUND -E 105900-35/ 1-B-ACE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| INDURE™ X210A-UV NATRL | LyondellBasell Industries | Polyolefin, Unspecified | INDURE™ |