Toyolac® 450Y MH1
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Plastics (Malaysia) Sdn. Bhd. |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l7Gs29_Toyolac-450Y-MH1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 450Y MH1 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or Europe. Important attributes of Toyolac® 450Y MH1 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 41.0 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 26 | % | ASTM D638 |
| Break | > 10 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 2060 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- 4 | 64.0 | MPa | ASTM D790 |
| -- 5 | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 190 | J/m | |
| 23°C, 12.7 mm | 170 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 98.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LA40 | Mando Advanced Materials Co., Ltd. | Nylon 66 | SEPAZ™ |
| Tekuform C27 | TEKUMA Kunststoff GmbH | Acetal (POM) Copolymer | Tekuform |
| BJB Polyurethane TC-400 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Europrene Latice® 2430 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Sylvin 9848-75FR Red 6137 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |