Versaflex™ OM 1360-9 Datasheet,TPE,PolyOne Corporation-SHANGHAI SUSHENG

Message
The Versaflex™ OM 1360-9 is designed for overmolding onto polycarbonate (PC), ABS, and PC/ABS susbstrates. Excellent Bond to PC, ABS, PC/ABS Rubbery Feel Soft Touch

General Information
Features	Good processing stability Soft
Uses	overmolding Electrical/Electronic Applications Soft touch application Soft handle Consumer goods application field
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.13	g/cm³	ASTM D792
Molding Shrinkage - Flow	0.90 - 2.1	%	ASTM D955

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shaw A, 10 seconds, 23°C)	60		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ASTM D412
100% strain, 23°C ²	1.79	MPa	ASTM D412
300% strain, 23°C ³	3.65	MPa	ASTM D412
Tensile Strength (Break, 23°C)	6.89	MPa	ASTM D412
Tensile Elongation (Break, 23°C)	650	%	ASTM D412

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 11200 sec^-1)	16.0	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	43.3 - 46.1	°C
Drying Time	3.0 - 4.0	hr
Suggested Max Moisture	< 0.030	%
Suggested Max Regrind	20	%
Rear Temperature	160 - 193	°C
Middle Temperature	177 - 193	°C
Front Temperature	182 - 204	°C
Nozzle Temperature	193 - 216	°C
Processing (Melt) Temp	182 - 216	°C
Mold Temperature	21.1 - 32.2	°C
Back Pressure	0.00 - 0.862	MPa
Screw Speed	75 - 125	rpm

Injection instructions
Color concentrates with EVA, polypropylene (PP) or LDPE carrier are most suitable for coloring Versaflex™ OM 1360-9. Typical letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Regrind levels up to 20% can be used with Versaflex™ OM 1360-9 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of the regrind effectiveness should be determined by the customer.Versaflex™ OM 1360-9 has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 5 - 8 minutes or longer.Suggested Dewpoint: -40°FInjection Speed: 1 to 3 in/sec1st Stage - Boost Pressure: 100 to 800 psi2nd Stage - Hold Pressure: 30% of BoostHold Time (Thick Part): 4 to 10 secHold Time (Thin Part): 1 to 3 sec

Injection instructions

Color concentrates with EVA, polypropylene (PP) or LDPE carrier are most suitable for coloring Versaflex™ OM 1360-9. Typical letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Regrind levels up to 20% can be used with Versaflex™ OM 1360-9 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of the regrind effectiveness should be determined by the customer.Versaflex™ OM 1360-9 has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 5 - 8 minutes or longer.Suggested Dewpoint: -40°FInjection Speed: 1 to 3 in/sec1st Stage - Boost Pressure: 100 to 800 psi2nd Stage - Hold Pressure: 30% of BoostHold Time (Thick Part): 4 to 10 secHold Time (Thin Part): 1 to 3 sec

Note Message
1 .	2 hours
2 .	Mouth die c
3 .	C mould

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	Versaflex™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	l5ZIal_Versaflex-OM-1360-9.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
UmaPET TF	Ester Industries Ltd.	PET	UmaPET
ARNYL PA66 30% FV INDUSTRIALE NERO	Daloga srl	Nylon 66	ARNYL
LNP™ THERMOCOMP™ RX05494 compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOCOMP™
Sylvin 2990-55 Clear 876	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
LNP™ STAT-LOY™ A3000T compound	SABIC Innovative Plastics	ABS	LNP™ STAT-LOY™