LNP™ THERMOCOMP™ DF008ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l4draf_LNP-THERMOCOMP-DF008ER-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DF008ER is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features include: Easy Molding, Mold Release. Also known as: LNP* THERMOCOMP* Compound DF-1008 EM MR Product reorder name: DF008ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.35 | % | ISO 294-4 |
| Flow : 24 hr | 0.16 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.93 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11800 | MPa | ASTM D638 |
| -- | 11200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 137 | MPa | ASTM D638 |
| Break | 136 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.3 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11300 | MPa | ASTM D790 |
| -- | 11000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 204 | MPa | ASTM D790 |
| -- | 203 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 220 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 810 | J/m | ASTM D4812 |
| 23°C 3 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.5 | J | ASTM D3763 |
| -- | 2.55 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 136 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 137 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinelec CCB6825 | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | Sinelec |
| Escorene™ Ultra UL 00514 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Hytrel® 21UV | DuPont Performance Polymers | TPC-ET | Hytrel® |
| I. Stern 870E | I. STERN & CO. INC. | PS (HIPS) | I. Stern |
| REV Materials 8009 | REV Materials | Polyolefin, Unspecified | REV Materials |