Keyflex® BT GN 7142F
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Keyflex® BT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l4XR5K_KeyflexBTGN7142F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Halogen Free Flame Retardant, Low Modulus Application Cable & Wire Jackets, Hose & Tubing |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C, Injection Molded) | 37 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 23°C, 2.00 mm, Injection Molded) | 7.85 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 2.00 mm, Injection Molded) | 700 | % | ASTM D638 |
| Flexural Modulus 3(23°C, 6.40 mm, Injection Molded) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40mm, injection molding | No Break | ASTM D256 | |
| 23°C, 6.40mm, injection molding | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 190 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C, 1.00 mm) | 24 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | V-0 | UL 94 | |
| 3.2 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 20 - 40 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 2 Temp. | 200 - 220 | °C | |
| Cylinder Zone 3 Temp. | 200 - 220 | °C | |
| Cylinder Zone 4 Temp. | 200 - 220 | °C | |
| Adapter Temperature | 200 - 220 | °C | |
| Melt Temperature | 190 - 230 | °C | |
| Die Temperature | 190 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC80-30I-504125-AGC | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| VITAMIDE® AR37BK8524 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Epoxies, Ect. 10-3046 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| HiFill® PA6/6 0249 B | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| SABIC® HDPE B5823 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |