ADVANCENE™ EM-6308-UV
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | ETHYDCO |
| Trademark: | ADVANCENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l4CItR_ADVANCENEEM6308UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADVANCENE™ EM-6308-UV High Density Polyethylene (HDPE) Resin is a narrow molecular weight distribution high density homopolymer designed to offer excellent stiffness, low warpage, good/acceptable toughness, and good moldability. This resin is ideally suited for injection molded crates, cases, trays; tote bins, and other objects requiring high rigidity. Main Characteristics:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.963 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/2.16 kg | 8.3 | g/10 min | ASTM D1238, ISO 1133 |
| 190°C/21.6 kg | 180 | g/10 min | ASTM D1238, ISO 1133 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 2.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 31.0 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 17.9 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 6.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 350 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 2% Secant | 1410 | MPa | ASTM D790B, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | |||
| -- 1 | 168 | kJ/m² | ASTM D1822 |
| -- | 168 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 84.0 | °C | ASTM D648, ISO 75-2/B |
| Brittleness Temperature | < -76.0 | °C | ASTM D746, ISO 974 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 133 | °C | ASTM D3418, ISO 3146 |
| Peak Crystallization Temperature (DSC) | 120 | °C | ASTM D3418, ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 260 | °C |
| Note Message | |
|---|---|
| 1 . | Type S |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT SG5151 | Sincerity Australia Pty Ltd. | PBT+PET | Sindustris PBT |
| TEKNIFLEX® MED 2001-0180 | Tekni-Films, a div of Tekni-Plex | Film, PP | TEKNIFLEX® MED |
| Taipol 4230 | TSRC Corporation | SBS | Taipol |
| Electrafil® PC 04007 | Techmer Engineered Solutions | PC | Electrafil® |
| Hy-Vin® XH79026 | INEOS Compounds | PVC, Flexible | Hy-Vin® |