ASTALAC™ ABS KMS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l44Emz_ASTALAC-ABS-KMS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS KMS was upgraded in November 2007 to comply with RoHS and is a high impact strength flame retardant grade of ABS designed for sheet extrusion applications requiring flame retardancy, superior toughness and abuse resistance whilst maintaining a balance of high gloss, easy formability and product rigidity. Typical thermoformed applications include large air conditioner/heater unit casings and advertising signage blanks. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS KMSUV ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 36.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 50 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2050 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 62.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 400 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 40.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 72.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 84.0 | °C | |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | AS/NZS 60695 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Cylinder Zone 1 Temp. | 170 to 190 | °C | |
| Cylinder Zone 2 Temp. | 175 to 200 | °C | |
| Cylinder Zone 3 Temp. | 180 to 205 | °C | |
| Cylinder Zone 4 Temp. | 185 to 210 | °C | |
| Cylinder Zone 5 Temp. | 190 to 220 | °C | |
| Melt Temperature | 190 to 230 | °C | |
| Die Temperature | 180 to 220 | °C | |
| Take-Off Roll | 75.0 to 105 | °C | |
| Back Pressure | 10.0 to 25.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene FRP256-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sylvin 5200-83C Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |
| Atlac 711-05AS | Reichhold Chemicals, Inc. | Polyester, TS | Atlac |
| HIPOLEN P® EA 5S | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| ICORENE® K1500 | ICO Polymers APAC, A Division of A. Schulman | XLPE | ICORENE® |