Victron® 095C2-WR
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | Victron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l43YGH_Victron-095C2-WR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyaryletherketones (Abbr. PEEK) is a crystalline high performance polymer with outstanding heat resistance, excellent strength and thermal properties. PEEK can compete with metals in lots of fields, its uniquely structure and properties offer outstanding fatigue and abrasion resistances, self-lubricated, excellent electrical properties, radiation resistance, and can withstand extreme temperatures difference environments. PEEK are highly used in electronics and electrical, automotives, mechanical and chemical, aerospace, military, and many high-end industries. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.60 | % | |
| Flow | 0.40 | % | |
| Water Absorption (Saturation, 23°C) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 145 | MPa | ISO 527-2/1270 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 8900 | MPa | ISO 178 |
| Flexural Stress 2 | 200 | MPa | ISO 178 |
| Abrasion (23°C) | 0.120 | ISO 8295 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 340 | °C | ISO 306/B50 |
| CLTE - Flow (-20 to 150°C) | 2.5E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.45 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+9 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® 8100 | Custom Resins Group | Nylon 612 | Nylene® |
| ALTECH® PE HD A 2040/500 GF40 | ALBIS PLASTIC GmbH | HDPE | ALTECH® PE |
| Daelim Po1y® LH-148 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Ferro PP LPP40BC93HB WHITE | Ferro Corporation | PP Homopolymer | Ferro PP |
| Electrafil® PC C BK | Techmer Engineered Solutions | PC | Electrafil® |