Honeywell PCTFE P2000HS

Category:	PCTFE , Polychlorotrifluoroethylene
Manufacturer:	Honeywell
Trademark:	Honeywell PCTFE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	l40Rq0_Honeywell-PCTFE-P2000HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Honeywell PCTFE P-Series HS film is a copolymer poly-chlor-tri-fluoroethylene film. Honeywell PCTFE HS film has the ability to heat seal to itself utilizing impulse sealing methods.

General Information
Features	Controlled rheology Heat sealable
Uses	Films
Forms	Films

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.08	g/cm³	ASTM D792

Films	Nominal Value	Unit	Test Method
secant modulus			ASTM D882
MD	1550	MPa	ASTM D882
TD	1380	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Fracture	62.1	MPa	ASTM D882
TD : Fracture	41.4	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	180	%	ASTM D882
TD : Fracture	200	%	ASTM D882
Water Vapor Transmission	0.25	g/m²/24 hr	ASTM E96

Thermal	Nominal Value	Unit	Test Method
Peak Crystallization Temperature (DSC)	190	°C	ASTM D3418

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	100	%	ASTM D2863

Optical	Nominal Value	Unit	Test Method
Haze	< 1.0	%	ASTM D1003

Additional Information
Yield: 6647 in²/lbTensile Strength @ Break, ASTM D 882, MD: 8000 to 10000 psiTensile Strength @ Break, ASTM D 882, TD: 5000 to 7000 psiElongation @ Break, ASTM 882, MD: 120 to 225%Elongation @ Break, ASTM 882, TD: 150 to 250%Secant Modulus, ASTM D 882, MD: 200000 to 250000 psiSecant Modulus, ASTM D 882, TD: 180000 to 220000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 350 g/milGraves Tear (initial), ASTM D 1004, TD: 250 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: -5 to -10% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: +5 to +10% shrinkageFlammability: Non-flammable

Additional Information

Yield: 6647 in²/lbTensile Strength @ Break, ASTM D 882, MD: 8000 to 10000 psiTensile Strength @ Break, ASTM D 882, TD: 5000 to 7000 psiElongation @ Break, ASTM 882, MD: 120 to 225%Elongation @ Break, ASTM 882, TD: 150 to 250%Secant Modulus, ASTM D 882, MD: 200000 to 250000 psiSecant Modulus, ASTM D 882, TD: 180000 to 220000 psiGraves Tear (initial), ASTM D 1004, MD: 325 to 350 g/milGraves Tear (initial), ASTM D 1004, TD: 250 to 325 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: -5 to -10% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: +5 to +10% shrinkageFlammability: Non-flammable

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X4298	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
RMA 57	Ronald Mark Associates, Inc.	PVC Homopolymer	RMA
Leona™ FH772	Asahi Kasei Chemicals Corporation	Nylon 66	Leona™
Lucent PP PPC-210	Lucent Polymers, Inc.	PP, Unspecified	Lucent PP
Sylvin 5132-75 Clear Pink 6233	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin