Arlon® 38N
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Arlon-MED |
| Trademark: | Arlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l1OGEe_Arlon-38N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 38N is an improved polyimide low-flow prepreg suitable for bonding multilayer polyimide rigid-flex, attaching heat sinks to polyimide MLBs, or other applications where minimal and uniform resin flow is required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption (24 hr) | < 1.0 | % | Internal Method |
| Decomposition Temperature | Internal Method | ||
| 5% | 330 | °C | |
| Intial | 311 | °C |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peel Strength | Internal Method | ||
| -- 1 | 1.5 | kN/m | |
| to Kapton 2 | 1.0 | kN/m | |
| to Kapton 3 | 0.9 | kN/m |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Expansion Rate (50 to 260°C) 4 | 1.5 | % | Internal Method |
| T260 | 50.0 | min | Internal Method |
| T288 | 5.0 | min | Internal Method |
| T300 | 3.0 | min | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 221 | MPa | Internal Method |
| Flexural Strength | 414 | MPa | Internal Method |
| Poisson's Ratio 5 | 0.17 | ASTM D3039 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 200 | °C | Internal Method |
| CLTE - Flow | |||
| -- 6 | 1.7E-5 | cm/cm/°C | Internal Method |
| < 200°C 7 | 5.4E-5 | cm/cm/°C | Internal Method |
| > 200°C 8 | 1.6E-4 | cm/cm/°C | Internal Method |
| Thermal Conductivity (100°C) | 0.30 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | Internal Method | ||
| -- 9 | 1.2E+15 | ohms | |
| -- 10 | 4.4E+12 | ohms | |
| Volume Resistivity | Internal Method | ||
| -- 11 | 4.7E+15 | ohms·cm | |
| -- 12 | 8.2E+13 | ohms·cm | |
| Dielectric Strength | 63 | kV/mm | Internal Method |
| Dielectric Constant (1 MHz) | 4.25 | Internal Method | |
| Dissipation Factor (1 MHz) | 0.010 | Internal Method | |
| Arc Resistance | 125 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | After Thermal Stress |
| 2 . | As Recieved |
| 3 . | After Solder |
| 4 . | Z-axis |
| 5 . | x and y direction |
| 6 . | X-axis |
| 7 . | Z-axis |
| 8 . | Z-axis |
| 9 . | E24/125 |
| 10 . | C96/35/90 |
| 11 . | E24/125 |
| 12 . | C96/35/90 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE 5000S | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| TechnoDur PBT-PET GF15 black (9970) | TechnoCompound GmbH | PBT+PET | TechnoDur |
| Fainplast PVC RH 210/W | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| EPAMOULD 786A33 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPAMOULD |
| Sylvin 9077-70 Grey 9534 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |