ExxonMobil™ LDPE LD 105 Series
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l1Cizy_ExxonMobil-LDPE-LD-105-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ExxonMobil LD 105 resins are homopolymer packaging film resins designed for applications requiring outstanding clarity with good stiffness. These resins can be processed in either blown or cast film equipment. In blown film equipment LD 105.30 can be drawn down to 1.0 mil gauge. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 214 | MPa | |
| 1% Secant, TD | 253 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.0 | MPa | |
| TD : Yield | 11.1 | MPa | |
| MD : Break | 25.1 | MPa | |
| TD : Break | 21.1 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 210 | % | |
| TD : Break | 570 | % | |
| Dart Drop Impact | 99 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 350 | g | |
| TD | 180 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 76 | ASTM D2457 | |
| Haze | 5.2 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 108950 E | RTP Company | Nylon 6 | RTP |
| Niuk 10TE15 | Shanghai Niuk New Plastic Technology Co., Ltd. | PP, Unspecified | Niuk |
| Axiall PVC 28930 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Gallonprene® GP520-6007 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| PENTAMID AHT GV30 H1 schwarz | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |