SCHULAMID® 66 GF 30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l0WwVQ_SCHULAMID66GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced PA 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 220 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 6200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 180 | 110 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 72 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 10 | -- | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -40°C | 60 | -- | kJ/m² | ISO 180/1U |
| 23°C | 65 | -- | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/Af |
| Ball Pressure Test (140°C) | Pass | -- | IEC 60695-10-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index | 600 | -- | °C | IEC 60695-2-12 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 60 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G1533HU-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Zythane® 4060D | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Karina CLEAR PVC COMPOUND -E 70/239-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Braskem PP H700-12 | Braskem America Inc. | PP Homopolymer | Braskem PP |
| LNP™ THERMOCOMP™ PF001S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |