PRE-ELEC® PA 1406
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l0Ivn1_PRE-ELEC-PA-1406.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PA 1406 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon fibre. In addition to a low electrical resistivity PRE-ELEC® PA 1406 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded technical parts and housings for electronic components and other static sensitive devices (SSD) when high rigidity is needed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 91.7 | MPa | ASTM D638 |
| 4.00 mm | 92.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 4.00 mm) | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 4960 | MPa | ASTM D790 |
| 4.00 mm | 5000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 2.1 | kJ/m² | ASTM D256 |
| -20°C | 3.0 | kJ/m² | ISO 179 |
| 23°C | 7.0 | kJ/m² | ISO 179 |
| 23°C | 6.3 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | 8.4 | kJ/m² | ASTM D256 |
| -20°C | 10 | kJ/m² | ISO 179 |
| 23°C | 20 | kJ/m² | ISO 179 |
| 23°C | 19 | kJ/m² | ASTM D256 |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 8.41 | kJ/m² | |
| 23°C, 4.00 mm | 8.41 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 37.8 | kJ/m² | |
| 23°C, 4.00 mm | 39.9 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | 38 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 214 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 193 | °C | ASTM D648A, ISO 75-2/Af |
| Vicat Softening Temperature | 217 | °C | ISO 306/A50, ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+7 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+5 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 80.0 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ratron® 250 | Asia International Enterprise (Hong Kong) Limited | PESU | Ratron® |
| StarTUFF TF 40-HR-1 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarTUFF |
| Geon™ Vinyl Flexible H41276D | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ICORENE® N1005 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| Bapolene® 4062NA | Bamberger Polymers, Inc. | PP Homopolymer | Bapolene® |