TUFLIN™ HS-7098C NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | TUFLIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | l06BRM_TUFLIN-HS-7098C-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TUFLIN™ HS-7098C NT 7 is an ethylene-hexene copolymer, linear low density polyethylene (LLDPE) resin designed for cast and blown film applications such as trash bags, industrial can liners, and retail bags. Films extruded with HS-7098C NT 7 exhibit superb toughness, high tensile strength and elongation, excellent tear and puncture resistance, and are readily heat sealable. Main Characteristics:
Application:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm | 44.8 | MPa | ASTM D882 |
| TD : Break, 25 µm | 34.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 500 | % | ASTM D882 |
| TD : Break, 25 µm | 700 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength 2 | ASTM D1922 | ||
| MD : 25 µm | 310 | g | ASTM D1922 |
| TD : 25 µm | 800 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (45°, 25.4 µm) | 45 | ASTM D523 | |
| Haze (25.4 µm) | 16 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 231 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm) 30:1 L/D 螺杆类型：DSBII 模具间隙：70 密尔 (1.8 mm) 熔体温度：448 °F (231 °C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5 比 1 螺杆速度：78 rpm 冷冻线高度：25 英寸 (635 mm) 1% 割线模量 |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-6063 | Ravago Manufacturing Americas, LLC | PP Impact Copolymer | Ravago Compounds |
| Ravago Compounds HM-257 | Ravago Manufacturing Americas, LLC | LDPE | Ravago Compounds |
| Wellamid® MR410 22H-WBK | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| KYDEX® XD03 | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |
| Eleme NGH200IG | Eleme Petrochemical Company Ltd | HDPE | Eleme |