Kepital® FG2025K
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kzugMU_Kepital-FG2025K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium viscosity grade for general injection molding. It was reinforced glass fiber, and so suitable for parts requiring very high stiffness, fatigue resistance, creep resistance, and heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.48 | g/cm³ | ASTM D792 |
| -- | 1.47 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 13 | g/10 min | ASTM D1238 |
| -- | 13 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 101 | MPa | ASTM D638 |
| Break, 23°C | 110 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 4.0 | % | ASTM D638 |
| Break, 23°C | 3.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5100 | MPa | ASTM D790 |
| 23°C | 4750 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 154 | MPa | ASTM D790 |
| 23°C | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 163 | °C | ASTM D648 |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1382 C AR 15 TFE 15 | RTP Company | PPS | RTP |
| Quantum Composites QC-8804 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| SCHULADUR® A GF 25 HF FR 1 | A. Schulman Europe | PBT | SCHULADUR® |
| Sinpolene CPP1040 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| Zhongfa PC G2830 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC | Zhongfa |