Hytrel® G5544

Category:	TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER
Manufacturer:	DuPont Performance Polymers
Trademark:	Hytrel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ky69Vl_Hytrel-G5544.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
55 Shore D Standard Performance Polyester Elastomer with Heat Ageing Protection

General Information
Additive	Heat Stabilizer
Features	Heat Stabilized
Uses	Blow Molding Applications Film Profiles Sheet
Agency Ratings	UL Unspecified Rating
Forms	Pellets
Processing Method	Blow Molding Casting Extrusion Film Extrusion Injection Molding Profile Extrusion Sheet Extrusion Thermoforming
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (TPE) (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	>TPC-ET<
Resin ID (ISO 1043)	TPC-ET

Physical	Nominal Value	Unit	Test Method
Density	1.22	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	10	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)	10.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	1.6	%
Flow	1.6	%
Water Absorption
24 hr	1.6	%	ASTM D570
23°C, 24 hr, 2.00 mm	2.2	%	ISO 62
Equilibrium, 23°C, 2.00 mm, 50% RH	0.40	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Shore Hardness			ISO 868
Shore D	56
Shore D, 15 sec	51

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	200	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Break	33.0	MPa
5.0% Strain	8.10	MPa
10% Strain	11.7	MPa
50% Strain	9.00	MPa
Tensile Strain (Break)	> 300	%	ISO 527-2
Nominal Tensile Strain at Break	290	%	ISO 527-2
Tensile Creep Modulus			ISO 899-1
1 hr	110	MPa
1000 hr	85.0	MPa
Flexural Modulus	190	MPa	ISO 178

Elastomers	Nominal Value	Unit	Test Method
Tear Strength			ISO 34-1
Across Flow	110	kN/m
Flow	120	kN/m

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-40°C	14	kJ/m²
-30°C	45	kJ/m²
23°C, Partial Break	90	kJ/m²
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1eU
Notched Izod Impact Strength			ISO 180/1A
-40°C	27	kJ/m²
23°C	64	kJ/m²
Tensile Impact Strength (23°C)	285	kJ/m²	ISO 8256/1

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	-61.0	°C	ISO 974
Glass Transition Temperature ¹	-35.0	°C	ISO 11357-2
Melting Temperature ²	214	°C	ISO 11357-3
CLTE			ISO 11359-2
Flow	2.1E-4	cm/cm/°C
Transverse	1.9E-4	cm/cm/°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+14	ohms	IEC 60093
Volume Resistivity	3.0E+12	ohms·cm	IEC 60093
Electric Strength	19	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	5.00
1 MHz	4.50
Dissipation Factor			IEC 60250
100 Hz	0.020
1 MHz	0.040

Flammability	Nominal Value	Unit	Test Method
Burning Rate (1.00 mm)	25	mm/min	ISO 3795
Flammability Classification			IEC 60695-11-10, -20
1.50 mm	HB
3.00 mm	HB
Oxygen Index	19	%	ISO 4589-2

Fill Analysis	Nominal Value	Unit	Test Method
Melt Density	1.05	g/cm³
Specific Heat Capacity of Melt	2110	J/kg/°C
Thermal Conductivity of Melt	0.15	W/m/K

Additional Information	Nominal Value	Unit	Test Method
Effective Thermal Diffusivity	0.0544	cSt
Odor	3		VDA 270

Note Message
1 .	10°C/min
2 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
RTP 3105	RTP Company	PFA	RTP
Sylvin 9658-45 Clear	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
HANWHA EVA 1328	Hanwha Chemical	EVA	HANWHA EVA
Hostacom M2 N01	LyondellBasell Industries	PP Homopolymer	Hostacom
Jiangsu Sinarise EX8535X	Jiangsu Sinarise New Material Technology Co., Ltd	TPE	Jiangsu Sinarise