Desmopan® DP 3491A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kxD2IL_Desmopan-DP-3491A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; suitable for extrusion blow molding; high mechanical strength; high melt stability; Application; Blow molding; Profiles; Injection molded engineering parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1200 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 92 | ||
| Shore D, 15 sec | 40 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 54.1 | MPa | |
| 10% Strain, 23°C | 3.90 | MPa | |
| 50% Strain, 23°C | 7.40 | MPa | |
| 100% Strain, 23°C | 8.90 | MPa | |
| 300% Strain, 23°C | 25.8 | MPa | |
| Tensile Strain 4(Break, 23°C) | 500 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 25.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 515 | MPa | |
| 20°C | 94.0 | MPa | |
| 60°C | 59.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 36 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5(23°C) | 100 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 20 | % | |
| 70°C, 24 hr | 50 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Melt Temperature | 180 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx WP63E30 | The Matrixx Group, Inc. | Nylon 6 | Matrixx |
| RTP 801 TFE 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| tefanyl® VR VRGR 921 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| Zytel® 101F BKB009 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| NORYL™ 731 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |