VESTAKEEP® 2000G
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAKEEP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kx2Iv9_VESTAKEEP-2000G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Medium-viscosity, unreinforced polyether ether ketone VESTAKEEP 2000G is a medium-viscosity, unreinforced polyether ether ketone for injection molding. The semi-crystalline polymer features superior thermal and chemical resistance. Parts made from VESTAKEEP 2000G are self-extinguishing. VESTAKEEP 2000G can be processed by common injection molding machines for thermoplastics. We recommend a melt temperature between 360°C and 380°C during the injection molding process. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (380°C/5.0 kg) | 70.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 80°C, 2.00 mm | 1.1 | % | |
| Flow : 80°C, 2.00 mm | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 100 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 30 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 6.0 | kJ/m² | |
| 23°C, Complete Break | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 335 | °C | ISO 306/A |
| -- | 310 | °C | ISO 306/B |
| Melting Temperature 2 | 340 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength 3 | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | ||
| 1 MHz | 2.80 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A 4 | 175 | V | |
| Solution A | 200 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 800 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 360 to 380 | °C | |
| Mold Temperature | 160 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | determined on 2 mm sheets with film gate at rim mold temperature 180°C |
| 2 . | 2nd heating |
| 3 . | K20/P50 |
| 4 . | 100 drops value |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 10642 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Unichem 9512G-05 | Colorite Polymers | PVC, Unspecified | Unichem |
| Dryflex® WS 73E150 | ELASTO | TPE | Dryflex® |
| Iupital® F20-73R1 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Karina GREEN PVC COMPOUND 861-40/27-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |