TRIPPS® 7A165
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIPPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kwO10o_TRIPPS-7A165.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIPPS® 7A165 is a Polyphenylene Sulfide (PPS) product. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) | 75 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 157 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 19600 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 196 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | 4.00 | ASTM D150 | |
| Dissipation Factor | 5.0E-3 | ASTM D150 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 84709 | RTP Company | PTT | RTP |
| Drystar™ 0113 | Eastman Chemical Company | Copolyester | Drystar™ |
| EPO-TEK® 320-3 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Elastollan® C 90 A 15 HPM 000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| LEXAN™ HFD1034 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |