Kynar Flex® 2950-05
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kwBkVf_Kynar-Flex-2950-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KYNAR FLEX® 2950-05 is a pelletized, semi-crystalline VF2 based copolymer. It has been designed for wire and cable applications requiring high flexibility and improved resistance to impact. The low molecular weight allows extrusion conditions that reduce jacket shrinkback over fiber optic constructions. ADDITIONAL CHARACTERISTICS: Excellent thermal stability Excellent abrasion resistance Excellent chemical resistance Impervious to UV degradation Self extinguising material Extremely low smoke emission characteristics Pigmentable |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.78 to 1.82 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 57 to 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 13.8 to 21.4 | MPa | |
| Break, 23°C | 20.0 to 27.6 | MPa | |
| Tensile Elongation (Break, 23°C) | 200 to 400 | % | ASTM D638 |
| Flexural Modulus (23°C) | 345 to 483 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 13.8 to 24.1 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 24.1 to 31.0 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 130 to 138 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 500 to 1200 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ren Ren Shape 550 | Huntsman Advanced Materials | PUR, Unspecified | Ren |
| TEREZ PA 6.6 7500 GF 15 GK 15 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Abstron IM17 SHG | Bhansali Engineering Polymers Limited | ABS+Acrylic | Abstron |
| Cheng Yu N6C3 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| Gallonprene® GP100-7502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |