Cri-Line LS-715
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Cri-Tech, Inc. |
| Trademark: | Cri-Line |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kvgPrY_Cri-Line-LS-715.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The LS compounds are designed to give part shrinkage (out of the mold) and post-curing operation comparable to a nitrile or similar elastomer. In most cases, tooling changes are not required when switching over to an LS compound. NPC indicates no post cure required to achieve high tensile and modulus values with good compression set and aging characteristics. FKHT is a high temperature resistant, low compression set compound. FKX is a high viscosity, high green strength, black fluorocarbon compound formulated for HAV and / or salt bath curing of O-ring cord and extruded profiles. |
| General Information |
|---|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.96 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 70 | MU |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Stress (100% Strain) | 4.41 | MPa | |
| Tensile Strength | 11.7 | MPa | |
| Tensile Elongation (Break) | 300 | % | |
| Compression Set 1(200°C, 22 hr) | 21 | % |
| Note Message | |
|---|---|
| 1 . | Plied discs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novodur® H801 | Styrolution | ABS | Novodur® |
| Durethan® BG 30 X F30 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| FORMULA P ELAN 5220 M2 Z | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Leona™ 1702 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Sylvin 9655-60 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |