Retpol® 3085/3 UVH NATURAL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kvdxGd_Retpol-3085-3-UVH-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extron 3085/3 UVH is a 40% glass fibre reinforced coupled polypropylene compound. It is a low flow injection moulding grade developed for thick walled components requiring excellent creep resistance with high heat deflection temperatures, high flexural modulus, high flexural strength and good impact strength. It has been stabilized to meet long term outdoor weathering requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.10 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 112 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 86 | ||
| Shore D, 15 sec, 3.00 mm | 79 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 116 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 850 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 630 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 162 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 154 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® SJ6300C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Fainplast PVC PHS 75/B | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Durez® 4400 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |