Durethan® BKV 60 XF 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kvDlWM_DurethanBKV60XF900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 60 % glass fibers, injection molding, improved flowability, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.69 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.76 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.52 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.070 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.25 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.050 | -- | % | ISO 2577 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 20200 | 13000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 215 | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.3 | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 18500 | 14000 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 350 | 230 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 2.6 | 2.8 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-220, GF60 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.20 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 88 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 15 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 80 | -- | kJ/m² | ISO 180/1U |
| 23°C | 80 | 75 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 3.40 | -- | J | ISO 6603-2 |
| 23°C | 4.20 | -- | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 950 | -- | N | ISO 6603-2 |
| 23°C | 1100 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 217 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 208 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 221 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.1E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Termaloy L-8040 | Proquigel | PC+ABS | Termaloy |
| DOW™ LLDPE DFDA-7047 NT 7 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| Borealis PE CG8410 | Borealis AG | HDPE | Borealis PE |
| Dryflex® 400901S | ELASTO | SBS | Dryflex® |
| FORMEX® GK-62 | ITW FORMEX | PP, Unspecified | FORMEX® |