TOTAL Polystyrene Impact 5240
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kvBKrL_TOTALPolystyreneImpact5240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYSTYRENE IMPACT 5240 is high heat resistant, high impact polystyrene for extrusion and injection applications. Applications Applications which require high heat resistance coupled with high impact. Hot fill, compounding, razors |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.3 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 76 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1850 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 26.0 | MPa | ISO 527-2 |
| Fracture | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 50 | % | ISO 527-2 |
| Flexural Modulus | 1850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, not annealed | 78.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 94.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Dielectric Strength | 150 | kV/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A3 GF 13 S3 black (3768) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ELASTOSIL® R plus 4020/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Hostacom PPR 4170L | LyondellBasell Industries | PP Homopolymer | Hostacom |
| INSULCAST® 333/INSULCURE 20 | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| POLYCOMPO PE 2208J | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |