Order Products : sales@su-jiao.com
Stanyl® TW241F8
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kux9wf_Stanyl-TW241F8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TW241F8 is a Polyamide 46 (Nylon 46) material filled with 40% glass fiber. It is available in Asia Pacific. Important attributes of Stanyl® TW241F8 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.51 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | 13000 | 8000 | MPa | |
| 120°C | 6900 | -- | MPa | |
| 160°C | 6100 | -- | MPa | |
| 180°C | 5700 | -- | MPa | |
| 200°C | 5300 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Break | 230 | 140 | MPa | |
| Break, 120°C | 130 | -- | MPa | |
| Break, 160°C | 115 | -- | MPa | |
| Break, 180°C | 105 | -- | MPa | |
| Break, 200°C | 100 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break | 3.0 | 6.0 | % | |
| Break, 120°C | 6.5 | -- | % | |
| Break, 160°C | 6.5 | -- | % | |
| Break, 180°C | 6.5 | -- | % | |
| Break, 200°C | 6.5 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -- | 11500 | 7000 | MPa | |
| 120°C | 5800 | -- | MPa | |
| 160°C | 5200 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | 12 | kJ/m² | |
| 23°C | 14 | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | 85 | kJ/m² | |
| 23°C | 95 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 12 | 12 | kJ/m² | |
| 23°C | 14 | 21 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C | |
| Thermal Index - 5000 hr | 177 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 300 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Syncure™ System S120NA | PolyOne Corporation | XLPE | Syncure™ |
| Gallonprene® GP310-8003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ISPLEN® PC 270 AV | REPSOL | PP Copolymer | ISPLEN® |
| LNP™ LUBRICOMP™ RFL26S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| LEXAN™ EXL8414 resin | SABIC Innovative Plastics | PC | LEXAN™ |