| PVC COMPOUND CLASS 70C (PVC/F) RECOMMENDED FOR INSULATION OF ELECTRICAL WIRES AND FLEXIBLE CORDS. ALSO SUITABLE FOR EXTRUSION OF NON STANDARD COAXIAL CABLE JACKET. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.43 to 1.47 | g/cm³ | IEC 60811-1-3 |
| Color | OK | ME 12 | |
| Color a | -1.70 to 0.300 | ME 12 | |
| Color b | 0.570 to 2.57 | ME 12 | |
| Color L | 90.5 to 92.5 | ME 12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Variation of Elongation | < 20 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 20 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 84 to 88 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 10.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 10.0 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -15.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | NBR 5403 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3100-22 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| WPP TPO TPO7510UV-Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| apirex® MBL 25 S | API SpA | TPU-Polyether | apirex® |
| KOPA® KN133G8ST | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Lupolen 3621 M RM Powder | LyondellBasell Industries | MDPE | Lupolen |