Order Products : sales@su-jiao.com
LNP™ THERMOCOMP™ LC008E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kuRreR_LNP-THERMOCOMP-LC008E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LC008E is a compound based on Polyetheretherketone resin containing 40% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound LC-1008 EM Product reorder name: LC008E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.73 | % | ISO 294-4 |
| Flow : 24 hr | 0.050 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 33100 | MPa | ASTM D638 |
| -- | 30500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 241 | MPa | ASTM D638 |
| Yield | 242 | MPa | ISO 527-2 |
| Break | 241 | MPa | ASTM D638 |
| Break | 242 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 1.3 | % | |
| Break | 1.3 | % | |
| Flexural Modulus | |||
| -- | 26900 | MPa | ASTM D790 |
| -- | 27500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 365 | MPa | ASTM D790 |
| -- | 352 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D4812 |
| 23°C 3 | 40 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.40 | J | ASTM D3763 |
| -- | 3.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 339 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 338 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 323 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 326 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 7.2E-6 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.0E-6 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® CD75FE | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| FRABUR 63 A | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRABUR |
| Elastamax™ HTE 3080 | PolyOne Corporation | PVC+NBR | Elastamax™ |
| Hyundai EP PPF HT121 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| LubriOne™ LB 6000-5006 NHFR NATURAL | PolyOne Corporation | Nylon 6 | LubriOne™ |