Marlex® D170DK
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ktDF6x_MarlexD170DK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
This metallocene linear low density polyethylene is an ethylene-hexene copolymer tailored for blown film applications that require:
Typical blown film applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.95 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.80 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 221 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 228 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 14.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 60.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 42.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 480 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 560 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | > 250 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 250 | g | ASTM D1922 |
| TD : 25 µm, blown film | 600 | g | ASTM D1922 |
| Seal Initiation Temperature 1(25 µm, Blown Film) | 109 | °C | ASTM F88 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.4 µm, Blown Film) | 100 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 10 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Temperature at which 0.3 lb/in heat seal strength is achieved. 0.5 s dwell, 30 psi pressure, 11.8 in/min separation rate. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren DJ210 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Kingfa PP-116 | Kingfa | PP, Unspecified | Kingfa |
| Kumho ABS 765 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Karina YELLOW COLOR CONCENTRATE 02/223-G | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pearlbond™ 100 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |