Ultramid® B3WG8 BK00564
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ksO9nI_Ultramid-B3WG8-BK00564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3WG8 BK 00564 is a 40% glass reinforced, pigmented black, heat stabilized injection molding PA6 grade. Applications Typical applications include pedals/pedal module. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12800 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 200 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 85 | kJ/m² | |
| 23°C | 95 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 10 | kJ/m² | |
| 23°C | 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| CLTE | |||
| Flow | 1.7E-5 | cm/cm/°C | |
| Transverse | 7.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech T706 | Shanghai Suptech Engineering Plastics Co. Ltd. | PBT | Sup-tech |
| Supol H-622 | Shanghai Suptech Engineering Plastics Co. Ltd. | TPO (POE) | Supol |
| Ferro PP LPP50BC73NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Jampilen RCXP598 | Jam Polypropylene Company | PP Random Copolymer | Jampilen |
| Lustran® ABS 556 | Styrolution | ABS | Lustran® ABS |