TAROMID A 280 G2 Y0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | krzgcO_TAROMID-A-280-G2-Y0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66 glass medium viscosity 10% glassifibres reinforced, heat stabilized, halogen free flame retardant UL94 V0, high electrical properties, good flow and mechanical properties as well as dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 - 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.80 - 1.1 | % | Internal method |
| Flow direction | 0.50 - 0.90 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.90 | % | ISO 62 |
| Saturated, 23°C | 6.6 | % | ISO 62 |
| Granule Humidity 1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 84.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.8 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 5100 | MPa | ISO 178 |
| Flexural Stress 3 | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 38 | J/m | ASTM D256 |
| Notched Izod Impact (23°C) | 3.70 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 206 | °C | ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 5 | 120 | °C | IEC 60216 |
| -- 6 | 150 | °C | IEC 60216 |
| Vicat Softening Temperature | 228 | °C | ISO 306/B50 |
| Ball Pressure Test (205°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 256 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 3.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 260 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| 5 . | 20,000 hr |
| 6 . | Short term |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2540A | Teknor Apex Company | TPE | Telcar® |
| THERMOLAST® K TF6STE (Series: FC/CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Braskem PP PRA 0852 | Braskem | PP Random Copolymer | Braskem PP |
| LEXAN™ HFD1014 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Lucky Enpla LPPC1000 | Lucky Enpla Co LTD | PPC | Lucky Enpla |