TAROMID B 280 Z2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | krDxHI_TAROMID-B-280-Z2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROMID B 280 Z2 is a polyamide 6 (nylon 6) product,. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 - 1.11 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.2 - 1.6 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.4 | % | ISO 62 |
| Saturated, 23°C | 7.0 | % | ISO 62 |
| Granule Humidity 1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 150 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2200 | MPa | ISO 178 |
| Flexural Stress 3 | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -25°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 200 | J/m | ASTM D256 |
| 23°C | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 62.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 220 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant | 3.00 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PURFLEX™ D67UV-BK | Pier One Polymers, Inc. | TPE | PURFLEX™ |
| Shin-Etsu RTV KE-3418 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Tecomid® NB30 MF30 BK001 HS | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| ALCOM® PC 740/4 CC1119-05LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| EVICOM™ RG7/915 | INEOS Compounds | PVC, Rigid | EVICOM™ |