Alathon® M5040
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kplMp6_Alathon-M5040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon M5040 is a copolymer with broad molecular weight distribution. This resin exhibits excellent color, low odor, and good processing stability. Typical applications for this resin are specialty applications with high ESCR and applications requiring a balance of ESCR, impact and processibility. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Spiral Flow | 28.4 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield 1 | 25.6 | MPa | |
| Break | 14.1 | MPa | |
| Tensile Elongation 2(Yield) | 13 | % | ASTM D638 |
| Flexural Modulus 3 | ASTM D790 | ||
| 1% Secant | 1040 | MPa | |
| 2% Secant | 862 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 66.1 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3857CT | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Wellamid® GFT13-66 XE-WT1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| TUFNYL® RGF 15 BLACK | SRF Ltd. | Nylon 66 | TUFNYL® |
| DINALEN® 65 | DIOKI d.d. | LDPE | DINALEN® |
| Karina PEARL COLOR CONCENTRATE 46/9-G | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |