Toyolac® 100-G10
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Plastics (Malaysia) Sdn. Bhd. |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kovVPu_Toyolac-100-G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 100-G10 is an Acrylonitrile Butadiene Styrene (ABS) material filled with 10% glass fiber. It is available in Asia Pacific or Europe. Important attributes of Toyolac® 100-G10 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 1 | 83.0 | MPa | ASTM D638 |
| Break | 75.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 2 | 3.0 | % | ASTM D638 |
| Break | > 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 3 | 4500 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- 4 | 130 | MPa | ASTM D790 |
| -- 5 | 129 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 12.7 mm) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® B BG6 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| Badadur® PBT8 FR HF | Bada AG | PBT | Badadur® |
| Fainplast PVC MGS 89 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| HAIPLEN EP60 T5 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| PENTAMID A A | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |