Makrolon® RW2407
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | koiVSa_Makrolon-RW2407.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 19 cm³/10 min; low viscosity; easy release; UV stabilized; variable content of filler for high reflectance application; injection molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.24 to 1.34 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 19.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 to 2700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 60.0 | MPa | |
| Break, 23°C | 50.0 to 60.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 5.5 | % | |
| Break, 23°C | 80 to 110 | % | |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength 1(23°C, Complete Break) | 15 | kJ/m² | ISO 7391 |
| Multi-Axial Instrumented Impact Energy (23°C) | 43.0 to 50.0 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 4800 to 5100 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| RTI Elec (1.50 mm) | 125 | °C | UL 746 |
| RTI Imp (1.50 mm) | 115 | °C | UL 746 |
| RTI Str (1.50 mm) | 125 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.70 mm, WT | HB | ||
| 3.00 mm, WT | HB | ||
| 0.750 mm, WT | V-2 | ||
| 1.50 mm, WT | V-2 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Light Reflection (4.00 mm) | 96.0 to 97.0 | JIS 8722 |
| Note Message | |
|---|---|
| 1 . | Based on ISO 180-A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTFA 25 | Polymer Tailoring Ltd. | Polyolefin, Unspecified | PTFA |
| RTP 803 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| Sindustris PC GN1001FA | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Alkathene® LD6622 | Qenos Pty Ltd | LDPE | Alkathene® |
| Kynar Flex® 3120-15 | Arkema | PVDF | Kynar Flex® |