Durethan® BKV 30 N1 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | knRpoz_Durethan-BKV-30-N1-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.58 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.60 | -- | % | |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.12 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.22 | -- | % | |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.040 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11700 | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress | ||||
| Yield, 23°C | -- | 80.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 140 | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ||||
| Yield, 23°C | -- | 3.5 | % | ISO 527-2/50 |
| Break, 23°C | 2.0 | 3.6 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | -- | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 11000 | 7500 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 230 | 145 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 2.5 | 3.5 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GFR, 14-120, GF30; ISO1043-PA GF FR (22) | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.070 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 8 | 5.00 | -- | J | |
| -- 9 | 7.00 | 9.00 | J |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | 12 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 45 | kJ/m² | |
| 23°C | 60 | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 50 | 45 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 135 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 10 | 225 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 28 | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.70 | 8.00 | ||
| 23°C, 1 MHz | 4.20 | 4.50 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.013 | 0.13 | ||
| 23°C, 1 MHz | 0.019 | 0.045 | ||
| Comparative Tracking Index | IEC 60112 | |||
| Solution A 11 | 350 | -- | V | |
| Solution B 12 | 125 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-1 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 2.00 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.60 mm | 775 | -- | °C | |
| 3.00 mm | 775 | -- | °C | |
| Oxygen Index 13 | 32 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | -30°C |
| 9 . | 23°C |
| 10 . | 10°C/min |
| 11 . | Depth of Erosion: 0.300 mm |
| 12 . | Depth of Erosion: 0.200 mm |
| 13 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 20GF GWT 960 | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Moplen RP320M | LyondellBasell Industries | PP Random Copolymer | Moplen |
| TEREZ PC/ASA Blend 1000 | TER HELL PLASTIC GMBH | ASA+PC | TEREZ PC/ASA |
| Altuglas® MI-8E | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| LOXIM 300 00 V0 | LOXIM Industries Private Limited | Nylon 6 | LOXIM |