Fiberfil® J-62/30/E
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | knMqKG_Fiberfil-J-62-30-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®J-62/30/E is a polypropylene copolymer (PP Copoly) material, which contains a 30% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main features of J-62/30/E are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.20 - 0.30 | % | ASTM D955 |
| 6.35 mm | 0.30 - 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 - 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4830 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 3.7 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 4480 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 136 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 146 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP TIVAR® 1000 UV Stabilized Natural | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| SABIC® LLDPE 118W | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Spartech Polycom EP5140 A1 | Spartech Polycom | PP Homopolymer | Spartech |
| Chemlon® 217 GIU | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Osterlene® PPH-30-.4 | Osterman & Company | PP Homopolymer | Osterlene® |