Lushan M-20A

Category:	Polyolefin, Unspecified , Polyolefin
Manufacturer:	Guangzhou Lushan New Materials Co., Ltd
Trademark:	Lushan
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kmwVg1_Lushan-M-20A.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Adhesive Resin for Multi-layer Oxygen Barrier Pipe Adhesive resin Lushan series for multi-layer oxygen barrier pipe is a modified polyolefin with functional groups. It's designed to bond to a variety of barrier materials, such as nylon and ethylene vinyl alcohol (EVOH), etc. Adhesive resin Lushan M-20A &M-12A have goods properties as below: High bonding strength, A wide range of bonding , Excellent chemical bonding with barrier materials EVOH & Nylon, Excellent heat resistance, weather resistance, chemical resistance, Excellent mechanical properties, Easy processing for adhesive resin, Hygiene and safety, non-toxic residues for adhesive resin, etc. Application: EVOH & Nylon

Message

Adhesive Resin for Multi-layer Oxygen Barrier Pipe

Adhesive resin Lushan series for multi-layer oxygen barrier pipe is a modified polyolefin with functional groups. It's designed to bond to a variety of barrier materials, such as nylon and ethylene vinyl alcohol (EVOH), etc.

Adhesive resin Lushan M-20A &M-12A have goods properties as below:

High bonding strength,

A wide range of bonding ,

Excellent chemical bonding with barrier materials EVOH & Nylon,

Excellent heat resistance, weather resistance, chemical resistance,

Excellent mechanical properties,

Easy processing for adhesive resin,

Hygiene and safety, non-toxic residues for adhesive resin, etc.

Application: EVOH & Nylon

General Information
Features	Bondability Good Chemical Resistance Good Processability Good Weather Resistance High Heat Resistance Oxygen Barrier
Uses	Adhesives Piping
Appearance	Clear/Transparent
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	0.909	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.1	g/10 min	ASTM D1238
Water Content	0.060	%	Internal Method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	19.0	MPa	ASTM D638
Tensile Elongation (Break)	750	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	75.0	°C	ASTM D1525
Peak Melting Temperature	120	°C	ASTM D2117

Resin Grade	Manufacturer	Category	Trademark
TABOND 2005	SILON s.ro	POP	TABOND
UTEC 3040	Braskem	UHMWPE	UTEC
Karina BLACK PVC COMPOUND -E 836-48/ 1-Y-CR	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LNP™ STAT-LOY™ 93000LTH compound	SABIC Innovative Plastics	Acrylic, Unspecified	LNP™ STAT-LOY™
SABIC® SUPEER™ 8112L	Saudi Basic Industries Corporation (SABIC)	mLLDPE	SABIC® SUPEER™