FERREX® GPP20CN05HB-WH
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kmLR8h_FERREX-GPP20CN05HB-WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FERREX® GPP20CN05HB-WH is a Polypropylene Homopolymer (PP Homopolymer) material filled with 22% calcium carbonate. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of FERREX® GPP20CN05HB-WH are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.4 | % | |
| Across Flow | 1.7 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 17.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 90 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 979 | MPa | |
| Tangent : 23°C | 1100 | MPa | |
| Flexural Strength (23°C) | 25.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Gardner Impact (23°C) | 27.3 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 113 | °C | |
| 1.8 MPa, Unannealed | 54.4 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 199 to 204 | °C | |
| Middle Temperature | 204 to 210 | °C | |
| Front Temperature | 210 to 216 | °C | |
| Nozzle Temperature | 216 to 221 | °C | |
| Mold Temperature | 46.1 to 60.0 | °C | |
| Back Pressure | 0.138 to 0.345 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 GA4S11 | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| STYRON A-TECH™ 1260 | Americas Styrenics LLC | PS (HIPS) | STYRON A-TECH™ |
| Kumho SAN SAN 300N A | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |
| ESTOPLAST XU 425NGY146 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |
| NORYL™ GFN1F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |