Braskem PE SLH118
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kmLCmO_Braskem-PE-SLH118.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SLH118 is a Linear Low Density Polyethylene, copolymer of hexene-1, produced by Spherilene process. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 40.0 | MPa | |
| TD : Break, 38 µm, Blown Film | 40.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Blown Film | 1100 | % | |
| TD : Break, 38 µm, Blown Film | 1400 | % | |
| Flexural Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Blown Film | 200 | MPa | |
| 1% Secant, TD : 38 µm, Blown Film | 210 | MPa | |
| Dart Drop Impact 1(38 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Blown Film | 300 | g | |
| TD : 38 µm, Blown Film | 510 | g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 84 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 1200-80A | RTP Company | TPU-Polyester | RTP |
| PULSE™ 2000 EZ | Trinseo | PC+ABS | PULSE™ |
| TOTAL Polypropylene PPC 1640 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| LNP™ COLORCOMP™ J1000R compound | SABIC Innovative Plastics Europe | PESU | LNP™ COLORCOMP™ |
| Sylvin 2971-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |