LNP™ THERMOCOMP™ WB006 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kmCevP_LNP-THERMOCOMP-WB006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP WB006 is a compound based on Polybutylene Terephalate resin containing Glass Bead. Also known as: LNP* THERMOCOMP* Compound WB-1006 Product reorder name: WB006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.57 | g/cm³ | ASTM D792 |
| -- | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 4.0 | % | |
| Across Flow : 24 hr | 1.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4080 | MPa | ASTM D638 |
| -- | 4210 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 54.0 | MPa | ASTM D638 |
| Break | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 4.2 | % | ASTM D638 |
| Yield | 3.7 | % | ISO 527-2/5 |
| Break 4 | 5.6 | % | ASTM D638 |
| Break | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 3980 | MPa | ASTM D790 |
| -- 6 | 3600 | MPa | ISO 178 |
| Flexural Strength 7(Break, 50.0 mm Span) | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 22 | J/m | ASTM D256 |
| 23°C 8 | 2.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D4812 |
| 23°C 9 | 12 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 4.00 | J | ASTM D3763 |
| -- | 0.900 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 186 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 170 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 93.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1399 X 130021 A | RTP Company | PPS | RTP |
| Bergamid™ A700 G35 H (f1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| BUP 630 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| Ducor® 1102 M | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| Vydyne® R525J NT0721 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |