Elastoskin® Lite 50555-05R Resin / S50555T Isocyanate

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	BASF Corporation
Trademark:	Elastoskin®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	klXuhP_ElastoskinLite5055505RResinS50555TIsocyanate.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Mechanial Air Assist Spray applied Polyurethane Elastomer used on the outer surface of automotive interior trim applications.

General Information
Uses	Application in Automobile Field Car interior parts

Physical	Nominal Value	Unit	Test Method
Density	0.760	g/cm³	ISO 1183/A

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	63		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress ¹			ISO 527-2/500
--	7.46	MPa	ISO 527-2/500
-- ²	5.90	MPa	ISO 527-2/500
-- ³	8.80	MPa	ISO 527-2/500
Tensile Strain			ISO 527-2/1B/500
Fracture	210	%	ISO 527-2/1B/500
Fracture ⁴	270	%	ISO 527-2/1B/500
Fracture ⁵	300	%	ISO 527-2/1B/500

Thermal	Nominal Value		Test Method
Cold Resistance ⁶(-40°C)	Pass		SAE J323

Flammability	Nominal Value	Unit	Test Method
Fogging	> 99.0		SAE J1756
Burning Rate	35	mm/min	Internal method

Additional Information
Liquid Components: Mix Ratio at 102 Index (by weight), Calculated: 100/53 (Resin/Isocyanate) Specific Gravity, Resin at 65°C, ASTM D1638: 1.0304 g/cm³ Specific Gravity, Isocyanate at 65°C, ASTM D1638: 1.202 g/cm³ Viscosity, Resin at 25°C, ASTM D2196: 1060 cps Viscosity, Isocyanate at 25°C, ASTM D2196: 700 cps Viscosity, Resin at 45°C, ASTM D2196: 400 cps Viscosity, Isocyanate at 45°C, ASTM D2196: 180 cps Viscosity, Resin at 65°C, ASTM D2196: 190 cps Viscosity, Isocyanate at 65°C, ASTM D2196: 50 cps Reactivity Hand Mix: Mix Ratio at 100 Index: 100/53 (Resin/Isocyanate) Chemical Temperatures: 25°C Mixer Speed: 3100 rpm Shyodu Gel Time: 23 to 27 sec

Additional Information

Liquid Components: Mix Ratio at 102 Index (by weight), Calculated: 100/53 (Resin/Isocyanate) Specific Gravity, Resin at 65°C, ASTM D1638: 1.0304 g/cm³ Specific Gravity, Isocyanate at 65°C, ASTM D1638: 1.202 g/cm³ Viscosity, Resin at 25°C, ASTM D2196: 1060 cps Viscosity, Isocyanate at 25°C, ASTM D2196: 700 cps Viscosity, Resin at 45°C, ASTM D2196: 400 cps Viscosity, Isocyanate at 45°C, ASTM D2196: 180 cps Viscosity, Resin at 65°C, ASTM D2196: 190 cps Viscosity, Isocyanate at 65°C, ASTM D2196: 50 cps Reactivity Hand Mix: Mix Ratio at 100 Index: 100/53 (Resin/Isocyanate) Chemical Temperatures: 25°C Mixer Speed: 3100 rpm Shyodu Gel Time: 23 to 27 sec

Note Message
1 .	Type 1B
2 .	Heat Aged, 500 hrs @ 121°C
3 .	Humid Aged, 168 hrs @ 80°C & 100% R.H.
4 .	Heat Aged, 500 hrs @ 121°C
5 .	Humid Aged, 168 hrs @ 80°C & 100% R.H.
6 .	Method A

Resin Grade	Manufacturer	Category	Trademark
TULAMID® PA-SM15	UCC Shchekinoazot	Nylon 6	TULAMID®
Niretan B C30	Soredi S.p.a.	Nylon 6	Niretan B
ALCOM® PA46 920/1 PTFE15	ALBIS PLASTIC GmbH	Nylon 46	ALCOM® PA46
LNP™ STAT-KON™ DEL339XF compound	SABIC Innovative Plastics	PC	LNP™ STAT-KON™
LEXAN™ XHT2146 resin	SABIC Innovative Plastics	PC	LEXAN™