GLS PP ZN09
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kl35FO_GLS-PP-ZN09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPHP PRECOLOR (unreinforced) |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.800 to 1.00 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 to 12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 32.0 to 34.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 6.0 | % | ASTM D638 |
| Flexural Modulus | 1400 to 1700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 25 to 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 52.0 to 56.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 32.0 to 65.0 | °C | |
| Injection Pressure | 68.0 to 105 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID B 280 Z1 G6 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| FORMULA P 6007 | Putsch Kunststoffe GmbH | PP, High Crystal | FORMULA P |
| Globalene® PT100 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| LNP™ LUBRICOMP™ XFL36 compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ LUBRICOMP™ |
| Sylvin 6185-80 Grey 935 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |