Bexloy® W Datasheet,Ionomer,DuPont Packaging & Industrial Polymers-SHANGHAI SUSHENG

Message
Bexloy® W is available in a variety of grades. The properties below represent the range of properties for most grades. Where only one number is listed, all grades are represented by that value. Bexloy® W modified ionomer resins were first engineered for injection molded exterior automotive applications such as molded-in-color fascia, bumper covers, side moldings and other decorative trim.

General Information
Features	Highlight stain resistance Recyclable materials Good color stability Good coloring Good wear resistance Low temperature impact resistance Scratch resistance Good wear resistance Good weather resistance
Uses	Application in Automobile Field Car interior parts Automotive exterior parts
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.963	g/cm³	ASTM D792
Molding Shrinkage - Flow	0.98	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	20.7	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	400	%	ASTM D638
Flexural Modulus - Tangent (23°C)	707	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	850	J/m	ASTM D256
Dart Drop Impact (-30°C)	36.2	J	ASTM D3029

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow (-30 to 80°C)	8.3E-5	cm/cm/°C	ASTM D696

Additional Information
The value listed as CLTE, ASTM 696, was tested in accordance with ASTM E831.Heat Sag, ASTM D3769, 152mm (6 in) Overhang, 30min, @ 180°F: 0.5inTear Resistance, ASTM D624, Die C, 508mm (20in)/min, @ 73°F: 850 to 970lb/inGardner Impact, ASTM D3209, -22°F: >320 in-lbRheometric Impact, ultimate energy, 5mph, 1/2in dia. Tup, 3in dia. Ring, 73°F: 194 in-lbRheometric Impact, ultimate energy, 5mph, 1/2in dia. Tup, 3in dia. Ring, -22°F: 159 in-lb3Elongation at Break, ASTM D638, 73°F: >400%Flexural Modulus, Tangent, 73°F, ASTM D790: 95 to 110 kpsiSpecific Gravity, 73°F, ASTM D792: 0.96 to 0.97Tensile Strength, 73°F, ASTM D638: 2800 to 3200 psiShrinkage, ASTM D955: 0.75 to 1.2%Coefficient of Linear Thermal Expansion, -22 to 176°F, ASTM E831: 4.2 to 5.0 x 10^-5

Additional Information

The value listed as CLTE, ASTM 696, was tested in accordance with ASTM E831.Heat Sag, ASTM D3769, 152mm (6 in) Overhang, 30min, @ 180°F: 0.5inTear Resistance, ASTM D624, Die C, 508mm (20in)/min, @ 73°F: 850 to 970lb/inGardner Impact, ASTM D3209, -22°F: >320 in-lbRheometric Impact, ultimate energy, 5mph, 1/2in dia. Tup, 3in dia. Ring, 73°F: 194 in-lbRheometric Impact, ultimate energy, 5mph, 1/2in dia. Tup, 3in dia. Ring, -22°F: 159 in-lb3Elongation at Break, ASTM D638, 73°F: >400%Flexural Modulus, Tangent, 73°F, ASTM D790: 95 to 110 kpsiSpecific Gravity, 73°F, ASTM D792: 0.96 to 0.97Tensile Strength, 73°F, ASTM D638: 2800 to 3200 psiShrinkage, ASTM D955: 0.75 to 1.2%Coefficient of Linear Thermal Expansion, -22 to 176°F, ASTM E831: 4.2 to 5.0 x 10^-5

Resin Grade	Manufacturer	Category	Trademark
Quadrant EPP Nylatron® GS	Quadrant Engineering Plastic Products	Nylon 66	Quadrant EPP
Trovidur® EN-F	Röchling Engineering Plastics SE & Co. KG	PVC, Rigid	Trovidur®
WONDERLITE® PC-6600	CHI MEI CORPORATION	PC	WONDERLITE®
Osterlene® LLDO-.9-918	Osterman & Company	LLDPE	Osterlene®
Kepamid® 2440GM7	Korea Engineering Plastics Co., Ltd	Nylon 66	Kepamid®

Category:	Ionomer , Ionomer
Manufacturer:	DuPont Packaging & Industrial Polymers
Trademark:	Bexloy®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kkneU9_Bexloy-W.pdf
PRICE:	Order Products email sales@su-jiao.com