LNP™ LUBRICOMP™ DFL34EH compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kknYLc_LNP-LUBRICOMP-DFL34EH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DFL34EH is a compound based on Polycarbonate containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Easy Molding, Healthcare, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4034 EM HC Product reorder name: DFL34EH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.48 | g/cm³ | |
| -- | 1.47 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.020 to 0.040 | % | |
| Across Flow : 24 hr | 0.20 to 0.40 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7190 | MPa | ASTM D638 |
| -- | 6650 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 95.0 | MPa | ASTM D638 |
| Break | 93.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 2.8 | % | ISO 527-2/5 |
| Break 3 | 2.7 | % | ASTM D638 |
| Break | 3.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 6320 | MPa | ASTM D790 |
| -- 5 | 6200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 150 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 145 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.50 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 13.0 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 89.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 7 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 740 | J/m | ASTM D4812 |
| 23°C 8 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 19.6 | J | ASTM D3763 |
| -- | 6.60 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 141 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.7E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F200 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Styropor® BF 395S | BASF Corporation | PS (EPS) | Styropor® |
| THERMOLAST® K TF7AAC (Series: FC/HE/tl) | KRAIBURG TPE | TPE | THERMOLAST® K |
| PolyFibra® PF-PEF05 | FuturaMat | PP, Unspecified | PolyFibra® |
| SD POLYCA™ CR3241 | Sumika Styron Polycarbonate Limited | PC+PET | SD POLYCA™ |