Isoplast® 300 ETPU
| Category: | ETPU , Engineering Thermoplastic Polyurethane |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Isoplast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kkDeZl_Isoplast-300-ETPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Isoplast® 300 is an engineering thermoplastic polyurethane resin. Appearance: Clear transparent pellets Application: Sheet extrusion, composite structures for industrial and consumer goods, injection molded parts. Feature: The Isoplast 300U ETPU contains a special UV stabilizer package. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/8.7 kg) | 5.0 - 17 | g/10 min | |
| Molding Shrinkage - Flow | 0.50 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec) | 83 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2130 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 63.0 | MPa | ISO 527-2/1A/5 |
| Fracture | 64.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 7.0 | % | ISO 527-2/1A/5 |
| Fracture | 170 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 1980 | MPa | ISO 178 |
| Flexural Stress | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 5.7 | kJ/m² | ISO 180/1A |
| 23°C | 8.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 79.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 69.0 | °C | ISO 75-2/A |
| Glass Transition Temperature | 90.0 | °C | DSC |
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 92.0 | % | ASTM D1003 |
| Yellowness Index | 15 | YI | ASTM D1925 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | < -30.0 | °C | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 205 - 215 | °C | |
| Middle Temperature | 215 - 225 | °C | |
| Front Temperature | 220 - 230 | °C | |
| Nozzle Temperature | 225 - 235 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Injection instructions |
|---|
| Feed Temperature: 40°CZone 4 Temperature: 225 to 235°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 205 - 215 | °C | |
| Cylinder Zone 2 Temp. | 210 - 220 | °C | |
| Cylinder Zone 3 Temp. | 215 - 225 | °C | |
| Cylinder Zone 4 Temp. | 220 - 230 | °C | |
| Adapter Temperature | 225 - 235 | °C | |
| Die Temperature | 230 - 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 3727WZ | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| NuSil G-9340 | NuSil Technology | Silicone | NuSil |
| Gallonprene® GP520-6004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| TECHNYL® C 206F NATURAL (R) | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| Sinkral® B 4 Venezia | Versalis S.p.A. | ABS | Sinkral® |