SABIC® PPcompound 19T1030
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | khxPG3_SABIC-PPcompound-19T1030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 19T1030 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding applications. The IMDS ID is 278628419. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 23°C, 48 hr | 1.3 | % | |
| Flow : 23°C, 48 hr | 0.75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4750 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 34.0 | MPa | ISO 527-2/50 |
| Break | 33.5 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | |
| Break | 4.0 | % | |
| Flexural Modulus 1(64.0 mm Span) | 4100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 2 | 1.4 | kJ/m² | |
| 23°C 3 | 1.9 | kJ/m² | |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 1.5 | kJ/m² | |
| 23°C | 1.6 | kJ/m² | |
| Instrumented Dart Impact 5(23°C, Energy at Peak Load) | 0.800 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed | 131 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 157 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 58.0 | µm/Mk | |
| Transverse : -30 to 100°C | 125 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4mm, Cut |
| 3 . | 80*10*4 mm, Cut |
| 4 . | 80*10*4mm, Cut |
| 5 . | 2.20 m/sec |
| 6 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP MPP25FA04WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Plenco 01508 (Injection) | Plastics Engineering Co. | Polyester, TS | Plenco |
| POLIMAXX 1100NK | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |
| Sylvin 6240-80 Red 6279 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Dow Corning® C6-530 | Dow Corning Corporation | Silicone | Dow Corning® |