Monprene® OM-12226
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | khuXrn_Monprene-OM-12226.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Monprene OM-12226 is designed for overmolding applications like grips and anti-skid parts for consumer products. Monprene OM-12226 is an opaque grade that exhibits excellent adhesion to PC, ABS, and PC/ABS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 29 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 26 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 0.538 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 0.676 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 1.23 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 1.59 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 6.83 | MPa | ASTM D412 |
| Flow : Fracture | 6.38 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 710 | % | ASTM D412 |
| Flow : Fracture | 700 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 15.2 | kN/m | ASTM D624 |
| Flow | 14.7 | kN/m | ASTM D624 |
| Compression Set 8(23°C, 22 hr) | 12 | % | ASTM D395B |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 138 - 188 | °C | |
| Middle Temperature | 154 - 199 | °C | |
| Front Temperature | 154 - 216 | °C | |
| Nozzle Temperature | 154 - 221 | °C | |
| Processing (Melt) Temp | 166 - 221 | °C | |
| Mold Temperature | 10.0 - 32.2 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 160 - 182 | °C | |
| Die Temperature | 160 - 182 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NatureFlex™ NVS 120 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| AVALON® 85 ABR | Huntsman Corporation | TPU-Polyester | AVALON® |
| Geon™ Vinyl Flexible A4DU6 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Electrafil® PA6 GF20 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| Osterlene® LD6521 | Osterman & Company | LDPE | Osterlene® |